| Product Type: | Fabric Tape | Thickness: | 390 µm |
|---|---|---|---|
| Backing: | Cloth | Adhesive: | Natural Rubber |
| Color: | White | Tensile: | 80 N/cm |
| Elongation: | 6% | Steel Peel: | 7.5 N/cm Initial, 7.6 N/cm After 14 Days |
| ST Temp: | 110 °C | Peel To ABS: | 7.3 N/cm Initial, 7.8 N/cm After 14 Days |
| Peel To Alu: | 7.2 N/cm Initial | Application: | Splicing Fabric Webs In Textile Production |
tesa 4964 | 390 µm Fabric Backing | Natural Rubber | 80 N/cm Tensile | 110 °C Short Term
Product Description
tesa 4964 is a double sided tape built on a flexible fabric backing that resists tearing, coated on both faces with natural rubber adhesive. The adhesive coat weight is high, which lets the tape sit down on rough and fibrous surfaces without losing contact. It lifts off most sound surfaces without leaving residue, though a trial is advisable before using it on plasticised material.
Structure
| Component | Material / Construction |
| Backing | flexible fabric (cloth), tear resistant |
| Adhesive | natural rubber, high coat weight, both sides |
| Release Liner | PV0 brown glassine paper, 71 µm |
Datasheet
| Property | Value |
| Total thickness | 390 µm |
| Backing | cloth |
| Adhesive | natural rubber |
| Color | white |
| Elongation at break | 6% |
| Tensile strength | 80 N/cm |
| Temperature resistance short term | 110 °C |
| Adhesion to steel | 7.5 N/cm initial, 7.6 N/cm after 14 days |
| Adhesion to ABS | 7.3 N/cm initial, 7.8 N/cm after 14 days |
| Adhesion to aluminium | 7.2 N/cm initial |
| Adhesion to PC | 7.4 N/cm initial |
| Adhesion to PE | 5.3 N/cm initial |
| Adhesion to PET | 6.5 N/cm initial, 7.2 N/cm after 14 days |
| Adhesion to PP | 6.8 N/cm initial |
| Adhesion to PS | 7.2 N/cm initial |
| Adhesion to PVC | 6.9 N/cm initial |